Product Description
PLA-Aero stands out as an innovative 3D printing material, expertly crafted for aeromodelling, ship models, drones, and beyond. This filament harnesses advanced temperature control techniques during printing to manage its foaming ratio, allowing for adjustable material density directly from the nozzle Harnessing the power of innovative material science, PLA-Aero is the ideal choice for projects where weight is critical without sacrificing structural integrity. Perfect for the dynamic needs of aeromodelling enthusiasts, drone builders, and ship model creators, PLA-Aero offers an edge with its lightweight composition and superior surface quality.
PLA-Aero is a PLA filament that will start foaming with the aid of a blowing agent during the printing process. The blowing agent is in an unexcited state in the PLA filament before printing. During the printing process，by adjusting the printing temperature, the foaming ratio of the blowing agent can be easily controlled. The maximum foaming ratio can reach 200%
Weight Efficiency:
Smooth Finish:
Versatility:
More about the product
Lorem ipsum dolor sit amet, consectetur adipisicing elit, sed do eiusmod tempor incididunt ut labore et dolore magna aliqua. Ut enim ad minim veniam, quis nostrud exercitation ullamco laboris nisi ut aliquip ex ea commodo consequat. Duis aute irure dolor in.
| Recommended Printing Settings | Physical Properties | Mechanical Properties | |||
|---|---|---|---|---|---|
| Drying Setting | 80℃， 8h | Desity | 1.03g/cm³ | Tensile Strength at Break (X-Y) | 8.25±0.15Mpa |
| Printing and keeping container's humidity | <20% RH | Vicat Softening Temp. | 80℃ | Breaking Elongation Rate | 11.52±0.58 % |
| Nozzle Temperature | 240~280℃ | Heat Deflection Temp. | 85℃ | Bending Modulus | 544.92±74.44 MPa |
| Bed Temperature | 80~90℃ | Melting Temperature | 204℃ | Bending Strength | 14.31±1.66 MPa |
| Printing Speed | 30-150mm/s | Melt flow Index | 1.56 ± 0.5g/10min | Notched Impact Strength | 2.29±0.13 KJ/㎡ |